Having immense experience of more than five decades in this domain, we are successfully engaged in offering quality assured Transparent Moulded Part PVC Compound. It is processed using top notch quality polyvinyl chloride and modern methodology with the help of dexterous professionals. Owing to its impurity free composition, the provided product is convenient for manufacturing transparent molded parts of machines, automobiles and medical equipment. Moreover, the offered Transparent Moulded Part PVC Compound is accessible from us at the most economical prices.

Key points:

  • Longer shelf life
  • Flame retardant
  • Precise composition
  • High clarity attribute

TECHNICAL DATA SHEET

  • Polyvinyl Chloride Compound
  • ER 315 GT is a high flow, medium impact, transparent compound ideally suited for variety of clear moulded components.

PROPERTIES

STANDARD

UNIT

TYPICAL VALUE

PHYSICAL

Appearance



Granular

Specific Gravity

ASTM D 792


1.32 ± 0.03

MECHANICAL

Hardness

ASTM D 2240

Shore D

73 + 3

Tensile Strength (min.)

ASTM D 638

MPa

60

Elongation at Break (min.)

ASTM D 638

%

18

Izod impact, notched 80x10x4 (23 °C) (min.)

ASTM D 256

KJ/M2

10

Flexural Modulus, 2 mm/min (min.)

ISO 178

MPa

2400

THERMAL

HDT/Be, 0.45 MPa edgew 120x10x4/s=100 mm

ASTM D 648

oC

60

Co efficient of linear thermal expansion

ISO 11359-2

%

8.1 x 10-5

RHEOLOGICAL

MVR (min.) (210 °C/20 Kg)

ASTM D 1238

cc /10 min

20

FLAMMABILITY

94V-0 Flame Class rating

UL 94

mm

1.00

Glow wire Test, 850 °C, Passes a

IEC 60695-2-12

mm

1.0

PROCESSING INFORMATION

Temperature Range


oC

165-180

Mould Shrinkage


cm/cm

0.045

For better results pre-drying of granules is recommended @ 75 ± 5°C for approximately 15 minutes